220KV和以下超高压超纯化学交联聚乙烯绝缘子 XEJ-220
Ultra-purity Chemical Cross-Linkable PE Insulation Compound for EHV Power Cable (≤220KV) ...
型号:0

参考价:¥

说:如果你对这个产品感兴趣,请在这里输入您的手机号码,把这个产品的地址 把它发到你的手机上。

Product description 产品描述
Chemical cross-linkable PE insulating compound for EHV power cable which regard advanced LDPE resin as the main material, adds antioxidant, cross-linking agent and other accessory addhesives, is manufactured by advanced closed extruder. It has excellent extrusion property and physical property, impurity content is controlled within limits. This product is mainly used for the insulation of High voltage &EHV cross-linking cables. It is applicable for 220KV and below cross-linking cables.
电力电缆用化学交联超高电压超纯聚乙烯隔热 是以高质量、低密度聚乙烯树脂为主要原料的隔热 ,添加抗氧化剂、交联剂和其他复配剂,采用先进的密闭混合装置进行加工,具有良好的挤出性能和物理性能,杂质含量符合要求,致力于高压生产、超高压交联电线电缆绝缘,本产品适用于220KV和下面的交联电线和电缆。
 
Processing Indicator 加工技术
Recommend to process with the PE extruder.
建议采用专用聚乙烯挤出机进行加工。


Model
品牌
Machine Barrel Temperature
汽缸温度
Molding Temperature
鼻温
XEJ-220 115-120℃ 118-120℃
 
Physical and Electrical Properties 物理和电学性质
Item
试点项目
Unit
单元
Standard Data
标准值
Density
密度
g/cm3 0.922±0.003
Tensile Strength
抗拉强度
MPa ≥17.0
Elongation at Break
断续扩展
% ≥450
20℃Volume Resistivity
20℃体积电阻
Ω·m ≥1.0×1014
20℃Dielectric Strength,50Hz
20℃介电强度, 50Hz
MV/m ≥30.0
20℃Dielectric Constant,50Hz
20℃介电常数, 50Hz
--- ≤2.3
20℃Dielectric Dissipation Factor,50Hz
20℃介质损耗因数, 50Hz
--- ≤0.0003
Impurity Content(Per 1.0Kg)
杂质含量(每1.0Kg)
100-250μm
250-625μm
>650 μm
 


 
0
0
0
Air Aging Condition
热风老化条件
135℃×168h
Tensile Strength Variation After Aging
抗拉强度变化率
% ±20
Elongation Variation After Aging
断裂伸长变化率
% ±20
Hot Set Test Condition
热延伸试验条件
200℃×0.2MPa×15min
Hot Elongation
荷载作用下延伸
% ≤75
Permanent Deformation After Cooling
冷却后永久变形
% ≤5